193.174.19.232Abstract: F. Almeraya-Calderon, M. Montoya-Rangel, D. Nieves-Mendoza, J. M. Jaquez-Mu noz, M. A. Baltazar-Zamora, L. Landa-Ruiz, M. Lara-Banda, E. Maldonado-Bandala, F. Estupi nan-Lopez, C. Gaona-Tiburcio (2024)

Metals, 14(11), 1208p. (2024) DOI:10.3390/met14111208

Frequency–Time Domain Analysis Based on Electrochemical Noise of Dual-Phase (DP) and Ferrite–Bainite (FB) Steels in Chloride Solutions for Automotive Applications

F. Almeraya-Calderon, M. Montoya-Rangel, D. Nieves-Mendoza, J. M. Jaquez-Mu noz, M. A. Baltazar-Zamora, L. Landa-Ruiz, M. Lara-Banda, E. Maldonado-Bandala, F. Estupi nan-Lopez, C. Gaona-Tiburcio

The automotive industry uses high-strength (HS), low-alloy (HSLA) steels and advanced high-strength steels (AHSSs) to manufacture front and rear rails and safety posts, as well as the car body, suspension, and chassis components of cars. These steels can be exposed to corrosive environments, such as in countries where de-icing salts are used. This research aims to characterize the corrosion behavior of AHSSs based on electrochemical noise (EN) [dual-phase (DP) and ferrite–bainite (FB)]. At room temperature, the steels were immersed in NaCl, CaCl2, and MgCl2 solutions and were studied by frequency–time domain analysis using wavelet decomposition, Hilbert–Huang analysis, and recurrence plots (RPs) related to the corrosion process and noise impedance (Zn). Optical microscopy (OM) was used to observe the microstructure of the tested samples. The results generally indicated that the main corrosion process is related to uniform corrosion. The corrosion behavior of AHSSs exposed to a NaCl solution could be related to the morphology of the phase constituents that are exposed to solutions with chlorides. The Zn results showed that DP780 presented a higher corrosion resistance with 918 Ω·cm2; meanwhile, FB780 presented 409 Ω·cm2 when exposed to NaCl. Also, the corrosion mechanism of materials begins with a localized corrosion process spreading to all the surfaces, generating a uniform corrosion process after some exposition time.

back

Creative Commons License © 2026 SOME RIGHTS RESERVED
The content of this web site is licensed under a Creative Commons Attribution-NonCommercial-NoDerivs 2.0 Germany License.

Please note: The abstracts of the bibliography database may underly other copyrights.

Ihr Browser versucht gerade eine Seite aus dem sogenannten Internet auszudrucken. Das Internet ist ein weltweites Netzwerk von Computern, das den Menschen ganz neue Möglichkeiten der Kommunikation bietet.

Da Politiker im Regelfall von neuen Dingen nichts verstehen, halten wir es für notwendig, sie davor zu schützen. Dies ist im beidseitigen Interesse, da unnötige Angstzustände bei Ihnen verhindert werden, ebenso wie es uns vor profilierungs- und machtsüchtigen Politikern schützt.

Sollten Sie der Meinung sein, dass Sie diese Internetseite dennoch sehen sollten, so können Sie jederzeit durch normalen Gebrauch eines Internetbrowsers darauf zugreifen. Dazu sind aber minimale Computerkenntnisse erforderlich. Sollten Sie diese nicht haben, vergessen Sie einfach dieses Internet und lassen uns in Ruhe.

Die Umgehung dieser Ausdrucksperre ist nach §95a UrhG verboten.

Mehr Informationen unter www.politiker-stopp.de.