Abstract: Z. Zhang, Z. Zhang, J. Tan, X. Wu (2019)

Stress corrosion cracking (SCC) of sensitized 304 stainless steel in high-temperature water was in-situ monitored by coupling acoustic emission (AE) and direct current potential drop (DCPD) techniques. The AE signals were identified using novel recurrence quantification analysis (RQA) and k-mean cluster method. It was found that the RQA is feasible to identify the evolution of different AE waveforms generated by ligament tearing and plastic deformation of the crack tip. The AE cumulative hits rate was linear with the SCC crack growth rate, providing a possibility for applying the AE technique to quantitatively evaluate SCC in high-temperature water.

Please note: The abstracts of the bibliography database may underly other copyrights.

Ihr Browser versucht gerade eine Seite aus dem sogenannten Internet auszudrucken. Das Internet ist ein weltweites Netzwerk von Computern, das den Menschen ganz neue Möglichkeiten der Kommunikation bietet.

Da Politiker im Regelfall von neuen Dingen nichts verstehen, halten wir es für notwendig, sie davor zu schützen. Dies ist im beidseitigen Interesse, da unnötige Angstzustände bei Ihnen verhindert werden, ebenso wie es uns vor profilierungs- und machtsüchtigen Politikern schützt.

Sollten Sie der Meinung sein, dass Sie diese Internetseite dennoch sehen sollten, so können Sie jederzeit durch normalen Gebrauch eines Internetbrowsers darauf zugreifen. Dazu sind aber minimale Computerkenntnisse erforderlich. Sollten Sie diese nicht haben, vergessen Sie einfach dieses Internet und lassen uns in Ruhe.

Die Umgehung dieser Ausdrucksperre ist nach §95a UrhG verboten.

Mehr Informationen unter www.politiker-stopp.de.

Quantitatively related acoustic emission signal with stress corrosion crack growth rate of sensitized 304 stainless steel in high-temperature water